Synthesis, characterisation and anti-corrosion screening of co(ii) n-methylcyclohexyl dithiocarbamate and co(ii) n-ethylcyclohexyl dithiocarbamate / Fasihah Esa

• Main Author: Esa, Fasihah
• Format: Student Project
• Language: English
• Published: Faculty of Applied Sciences 2017
• Subjects: QD Chemistry; Metals; Dyes
• Online Access: http://ir.uitm.edu.my/id/eprint/26853/1/PPb_FASIHAH%20ESA%20AS%20N%2017_5.pdf; http://ir.uitm.edu.my/id/eprint/26853/
• Institution: Universiti Teknologi Mara

The new series of cobalt(II) dithiocarbamate complexes were successfully synthesised by using 'in situ' method with ethanol. The amines used in this study were N-methylcyclohexylamine and N-ethylcyclohexylamine. The dithiocarbamate complexes were characterised by using Ultraviolet Visible Spectroscopy (UV-Vis), Fourier Transform Infrared Spectroscopy (FTIR) and molar conductivity. The Co(II) dithiocarbamate complexes were acted as an inhibitor corrosion on mild steel. The data of UV-Vis and FTIR showed an agreement with proposed structures of Co(II) dithiocarbamate complexes. The UV-Visible analysis showed two types of transitions which are n -----+ n * and n-----+ n*. The electronic spectra of d-d transition appeared at >400 nm and indicate that the Co(II) was successfully coordinated to the dithiocarbamate ligands. Infrared spectra of the complexes showed that the thiouride band, ·v(C=N) appeared at 1470 -1480 cm- 1. The stretching band ofv(C=S) was unsplitting and the region was appeared at range 1010 - 1013 cm- 1 indicates that's the behaviour of dithiocarbamate complexes is a bidentate. The molar conductivity of Co(II) dithiocarbamate complexes showed that there was a non-electrolyte. The gravimetric analysis showed the percentages of Co(II) complexes were 15.90% in Co(II) N-methylcyclohexyl dithiocarbamate and 14.75% in Co(II) Nethylcyclohexyl dithiocarbamate that exactly same as a calculated amount. The inhibition effects of corrosion on the mild steel were investigated by weight loss method. The inhibitor efficiency was increased as the concentration of inhibitor increased and indicates that the dithiocarbamate complexes were adsorbed on the surface of the mild steel. The efficiency of corrosion inhibitor for Co(II) Nmethylcyclohexyl dithiocarbamate is better than Co(II) N-ethylcyclohexyl dithiocarbamate.