Bi-relaxation behaviors in epitaxial multiferroic double-Perovskite BiFe0.5Mn0.5O3/CaRuO3 heterostructures
Multiferroic double-perovskite BiFe0.5Mn0.5O3 thin film heterostructures were epitaxially grown on CaRuO3-buffered (001) SrTiO3 by pulse laser deposition. Typical Vogel-Fulcher relaxorlike dielectric and magnetic susceptibilities were observed, implying the film exhibits the properties of an electri...
Saved in:
| Main Authors: | , , , , |
|---|---|
| 格式: | Article |
| 語言: | English |
| 出版: |
AIP Publishing
2011
|
| 主題: | |
| 在線閱讀: | http://eprints.um.edu.my/8236/1/Miao-2011-Bi-relaxation_behavi.pdf http://eprints.um.edu.my/8236/ http://apl.aip.org/resource/1/applab/v99/i6/p062905_s1 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 機構: | Universiti Malaya |
| 語言: | English |
| 總結: | Multiferroic double-perovskite BiFe0.5Mn0.5O3 thin film heterostructures were epitaxially grown on CaRuO3-buffered (001) SrTiO3 by pulse laser deposition. Typical Vogel-Fulcher relaxorlike dielectric and magnetic susceptibilities were observed, implying the film exhibits the properties of an electric relaxor and a magnetic relaxor. Polarization and size of polar nanoregions (PNRs) were determined by fitting the dielectric constant to a multi-polarization mechanism model. It was found that PNRs of 7-11 nm decrease from 0.67 mu C/cm(2) to 0.11 mu C/cm(2), as the temperature increases from 380 K to 460 K. A weak ferromagnetism was observed via magnetic hysteresis loops up to 300 K. (C) 2011 American Institute of Physics. [doi:10.1063/1.3624847] |
|---|