Behavior of defects in a-plane GaN films grown by low-angle-incidence microchannel epitaxy (LAIMCE)
The microstructure in a-plane GaN thin films was characterized by transmission electron microscopy. The GaN thin films were grown by metal-organic molecular beam epitaxy (MOMBE) on a GaN/r-plane sapphire template using the low-angle-incidence microchannel epitaxy (LAIMCE) technique, following fabric...
Saved in:
Main Authors: | , , , , , , , |
---|---|
Format: | Article |
Published: |
Elsevier B.V.
2014
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/51987/ http://dx.doi.org/10.1016/j.jcrysgro.2013.11.032 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Universiti Teknologi Malaysia |
Summary: | The microstructure in a-plane GaN thin films was characterized by transmission electron microscopy. The GaN thin films were grown by metal-organic molecular beam epitaxy (MOMBE) on a GaN/r-plane sapphire template using the low-angle-incidence microchannel epitaxy (LAIMCE) technique, following fabrication of a stripe type mask. The polar direction +c at GaN thin films was determined from the electron diffraction pattern by the relationship between c-axis of sapphire and +c of nitride crystal. It was confirmed that threading dislocations passing through the mask windows penetrate into the overgrown GaN layer, running straight up to the Lop surface without bending. Therefore wing regions containing fewer lattice defects are successfully formed. The density of lattice defects is roughly estimated to be around 10(8) cm(-2). Stacking faults (SFs) and partial dislocations on the edges of SFs on the basal planes are found to be formed additionally in the wing regions. As GaN islands that have been formed on the mask windows grow first laterally along +c and -c direction, the microstructures in the c and owing regions were predicted to be different from each other. Bur actually, they are almost the same as each other due to the fact that the islands of GaN develop laterally with the a-plane growth process instead of c-plane growth. |
---|