Influence of reaction time on optical property of ZnS:Mn nanoparticles synthesized by a hydrothermal method
ZnS:Mn (CMn = 5 %mol) nanoparticles have been synthesized by a hydrothermal method from solutions of Zn(CH3COO)2 0.1 M, Na2S2O3 0.1 M and Mn(CH3COO)2 0.01 M at 220oC for different reaction time. The result showed that increasing reaction time from 3 to 30h almost does not change cubic crystalline s...
محفوظ في:
| المؤلفون الرئيسيون: | , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
H. : ĐHQGHN
2017
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://repository.vnu.edu.vn/handle/VNU_123/55390 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Vietnam National University, Hanoi |
| اللغة: | English |
| الملخص: | ZnS:Mn (CMn = 5 %mol) nanoparticles have been synthesized by a hydrothermal method from solutions of Zn(CH3COO)2 0.1 M, Na2S2O3 0.1 M and Mn(CH3COO)2 0.01 M at 220oC for different reaction time. The result showed that increasing reaction time from 3 to 30h almost does not change cubic crystalline structure, peak positions attributed to Mn2+ ions at 585 nm in photoluminescence spectra and 392, 430, 463, 468, 492 nm in photoluminescence excitation spectra when monitoring the 585 nm band of ZnS:Mn nanoparticles but only slight increases lattice constant, the average particle size and changing their intensity. As increasing the reaction time from 3 to 10h, intensity of bands attributed to Mn2+ ions also increase, reaches the maximum at 15h and then decreases as increasing reaction time to 30 h. Cause of these phenomena have been investigated and reported. |
|---|