Preparation and Characterization of NiO/YSZ and Ni/YSZ Porous Composite Electrodes Synthesized via Glycine-Nitrate Combustion Process
Electrode materials require a good porosity and a fine microstructure in order to maximize the triple phase boundary between the electronic conductor, ionic conductor and the gases involved in the reaction. In this study, NiO/YSZ composite, one of the most desired candidates as a cathode material fo...
Saved in:
| Main Authors: | , |
|---|---|
| 格式: | text |
| 出版: |
Archīum Ateneo
2019
|
| 主題: | |
| 在線閱讀: | https://archium.ateneo.edu/chemistry-faculty-pubs/168 https://www.scientific.net/KEM.801.205 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Electrode materials require a good porosity and a fine microstructure in order to maximize the triple phase boundary between the electronic conductor, ionic conductor and the gases involved in the reaction. In this study, NiO/YSZ composite, one of the most desired candidates as a cathode material for solid oxide electrolysis cells, was synthesized via glycine-nitrate combustion process. The composite powder was mixed with carbon black pore former in order to increase the porosity of NiO/YSZ. The samples were sintered at 1300 °C and subsequently reduced. X-ray diffraction patterns of the as-reduced samples confirm the transformation of NiO to Ni phase. Scanning electron microscopy and energy dispersive spectroscopy (SEM/EDS) images were able to confirm the reduction of NiO to Ni. From the results of the electrochemical impedance spectroscopy analysis, the total conductivity of Ni/YSZ at 700 °C were about 1.37 × 10-1 and 1.12 × 10-1 S/cm for the unmodified and carbon black-modified samples, respectively. |
|---|