Vanadium oxide thin film formation on graphene oxide by microexplosive decomposition of ammonium peroxovanadate and its application as a sodium ion battery anode
Formation of vanadium oxide nanofilm-coated graphene oxide (GO) is achieved by thermally induced explosive disintegration of a microcrystalline ammonium peroxovanadate-GO composite. GO sheets isolate the microcrystalline grains and capture and contain the microexplosion products, resulting in the de...
Saved in:
| Main Authors: | , , , , , , , , , |
|---|---|
| 其他作者: | |
| 格式: | Article |
| 語言: | English |
| 出版: |
2020
|
| 主題: | |
| 在線閱讀: | https://hdl.handle.net/10356/142082 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Formation of vanadium oxide nanofilm-coated graphene oxide (GO) is achieved by thermally induced explosive disintegration of a microcrystalline ammonium peroxovanadate-GO composite. GO sheets isolate the microcrystalline grains and capture and contain the microexplosion products, resulting in the deposition of the nanoscale products on the GO. Thermal treatment of the supported nanofilm yields a sequence of nanocrystalline phases of vanadium oxide (V3O7, VO2) as a function of temperature. This is the first demonstration of microexplosive disintegration of a crystalline peroxo compound to yield a nanocoating. The large number of recently reported peroxide-rich crystalline materials suggests that the process can be a useful general route for nanofilm formation. The V3O7@GO composite product was tested as a sodium ion battery anode and showed high charge capacity at high rate charge-discharge cycling (150 mAh g-1 at 3000 mA g-1 vs 300 mAh g-1 at 100 mA g-1) due to the nanomorphology of the vanadium oxide. |
|---|