Phase and electrical properties of PZT thin films embedded with CuO nano-particles by a hybrid sol-gel route

• المؤلفون الرئيسيون: Tharathip Sreesattabud, Brady J. Gibbons, Anucha Watcharapasorn, Sukanda Jiansirisomboon
• التنسيق: دورية
• منشور في: 2018
• الوصول للمادة أونلاين: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84880439079&origin=inward; http://cmuir.cmu.ac.th/jspui/handle/6653943832/47832
• المؤسسة: Chiang Mai University

Pb(Zr 0.52 Ti 0.48 )O 3 or PZT thin films embedded with CuO nano-particles were successfully prepared by a hybrid sol-gel process. In this process, CuO (0, 0.1, 0.2, 0.3, 0.4, 0.5 and 1 wt. %) nanopowder was suspended in an organometallic solution of PZT, and then coated on platinised silicon substrate using a spin-coating technique. The influence of CuO nano-particles' dispersion on the phase of PZT thin films was investigated. XRD results showed a perovskite phase in all films. At the CuO concentration of 0.4-1 wt. %, a second phase was observed. The addition of CuO nano-particles affected the orientation of PZT thin films. The addition was also found to reduce the ferroelectric properties of PZT thin films. However, at 0.2 wt. % CuO concentration, the film exhibited good ferroelectric properties similar to those of PZT films. In addition, the fatigue retention properties of the PZT/CuO system was observed, and it showed 14% fatigue at 10 8 switching bipolar pulse cycles while the fatigue in PZT thin films was found to be 17% at the same switching bipolar pulse cycles. © 2013 The Korean Institute of Metals and Materials and Springer Science+Business Media Dordrecht.