Enhanced electrical properties of lead-free BNLT-BZT ceramics by thermal treatment technique
Electrical properties of lead-free solid solution ceramics from the Bi 0.4871 Na 0.4871 La 0.0172 TiO 3 (BNLT) and BaZr 0.05 Ti 0.95 O 3 (BZT) system have been improved by a thermal treatment technique. A modified two step mixed-oxide method was employed for the preparation of the (1-x)BNLT-xBZT cer...
Saved in:
| Main Authors: | , , |
|---|---|
| 格式: | 雜誌 |
| 出版: |
2018
|
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84875723539&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/47930 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Electrical properties of lead-free solid solution ceramics from the Bi 0.4871 Na 0.4871 La 0.0172 TiO 3 (BNLT) and BaZr 0.05 Ti 0.95 O 3 (BZT) system have been improved by a thermal treatment technique. A modified two step mixed-oxide method was employed for the preparation of the (1-x)BNLT-xBZT ceramics, where x=0.06, 0.09, 0.12 and 0.20. After sintering at 1125 °C for 4 h, the BNLT-BZT ceramics were annealed at 825, 925 and 1025 °C. The annealing treatment caused an increase in dielectric constant of BNLT-BZT ceramics with x≤0.09 mol% and with x higher than 0.09 mol% the dielectric value dropped considerably. The ferroelectric properties of all annealed ceramic samples tend to decrease with increasing annealing temperature as confirmed by the slimmer P-E loops. The piezoelectric coefficient (d 33 ) increased with annealing temperatures and a maximum value of ∼170 pC/N was obtained from the ceramic samples annealed at 1025 °C with x=0.02. © 2012 Elsevier Ltd and Techna Group S.r.l. |
|---|