Effects of la-dopant on phase, microstructure and dielectric properties of Bi4Ti3O12 ceramics
Bi4-xLaxTi3O12 (where x = 0, 0.25, 0.50, 0.75 and 1) powders and ceramics were prepared using conventional solid state reaction and sintering procedures. The calcination was carried out at 750 °C for 4 h and sintering was done at 1150 °C for 4 h. The density of all ceramics was found to be comparabl...
Saved in:
| Main Authors: | , , |
|---|---|
| 格式: | Book Series |
| 出版: |
2018
|
| 主題: | |
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=75649119660&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/50861 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Bi4-xLaxTi3O12 (where x = 0, 0.25, 0.50, 0.75 and 1) powders and ceramics were prepared using conventional solid state reaction and sintering procedures. The calcination was carried out at 750 °C for 4 h and sintering was done at 1150 °C for 4 h. The density of all ceramics was found to be comparable regardless of La concentration. X-ray diffraction analysis showed that preferred orientation of ceramic grains was reduced with addition of La ions. This reduced preferred orientation was accompanied by a decrease in grain size. The temperature dependence of dielectric constant showed a decrease in Tc with increasing La concentration. © (2010) Trans Tech Publications. |
|---|