Formation of nano-sodium niobate crystals in ferroelectric glasses and glass-ceramics of the Na2O-Nb2O5-Al 2O3-SiO2 system
Ferroelectric glasses and glass-ceramics were prepared from selected composition in the Na2O-Nb2O5-Al2O3-SiO2 glass system. Small amount of TiO2 was also added. Conventional melt-quenching technique was employed for a glass production and the selected bulk parent glass samples were subjected to the...
Saved in:
| Main Authors: | , , |
|---|---|
| 格式: | Conference or Workshop Item |
| 語言: | English |
| 出版: |
2014
|
| 在線閱讀: | http://www.scopus.com/inward/record.url?eid=2-s2.0-77749328408&partnerID=40&md5=e7b03299b6481067672979d8be4f0844 http://cmuir.cmu.ac.th/handle/6653943832/5729 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Ferroelectric glasses and glass-ceramics were prepared from selected composition in the Na2O-Nb2O5-Al2O3-SiO2 glass system. Small amount of TiO2 was also added. Conventional melt-quenching technique was employed for a glass production and the selected bulk parent glass samples were subjected to the heat-treatment process. Clear transparent glass was obtained but with surprise presence of precipitated nano-size NaNO3 crystals as the result of phase separation. For the heat-treated samples, the longer treatment time induced a higher volume fraction of the NaNbO3 crystals, but thier size was not significantly increased. Dielectric response of the glass-ceramics contained NaNbO3 crystals is the combination of all contribution from both crystalline phases and the glass matrix. Copyright © Taylor & Francis Group, LLC. |
|---|