Effect of excess PbO on microstructure and mechanical properties of (Pb<inf>0.975</inf>Ba<inf>0.025</inf>)ZrO<inf>3</inf>ceramics
(Pb0.975Ba0.025)ZrO3(PBZ2.5) ceramics were fabricated from their oxide mixture via the solid state reaction method. Excess PbO (1, 3, 5 and 10 wt%) was added together with starting materials to compensate for PbO loss from evaporation during calcination and sintering. The phase structure was analyze...
Saved in:
| Main Authors: | , |
|---|---|
| 格式: | 雜誌 |
| 出版: |
2018
|
| 主題: | |
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=33744519847&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/61754 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | (Pb0.975Ba0.025)ZrO3(PBZ2.5) ceramics were fabricated from their oxide mixture via the solid state reaction method. Excess PbO (1, 3, 5 and 10 wt%) was added together with starting materials to compensate for PbO loss from evaporation during calcination and sintering. The phase structure was analyzed by XRD. Pure PBZ2.5 phase was observed in all of the PBZ2.5 samples. Density, dielectric and mechanical properties were measured. The experimental results suggest that 1 wt% excess PbO is the optimal level to obtain the best properties of the ceramics. The results were discussed in terms of the mechanisms of densification. © 2005 Elsevier B.V. All rights reserved. |
|---|