SYNTHESIS OF ACTIVATED CARBON FROM SALACCA PEEL WITH HYDROTHERMAL CARBONIZATION FOR SUPERCAPACITOR APPLICATION
Supercapacitor is considered as promising technology in energy storage system (EES) because of high power, large currents, and excellent cycle stability. In this study, activated carbon was used as the constituent material for electrodes because it owns porous structure with large surface area, o...
Saved in:
| Main Author: | |
|---|---|
| Format: | Theses |
| Language: | Indonesia |
| Online Access: | https://digilib.itb.ac.id/gdl/view/42262 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Institut Teknologi Bandung |
| Language: | Indonesia |
| Summary: | Supercapacitor is considered as promising technology in energy storage system
(EES) because of high power, large currents, and excellent cycle stability. In this
study, activated carbon was used as the constituent material for electrodes
because it owns porous structure with large surface area, owns high conductivity,
low cost, and renewable. Activated carbon was synthesized from salacca peel by
hydrothermal carbonization and chemical activation with KOH. Salacca peel was
chosen as a precursor because it has high fixed carbon content and low ash
content, but usually discarded as a waste.
This research focused on the effect of operating pressure in the hydrothermal
carbonization process. The the operating pressure used will determine the water
phase in the hydrothermal process, where in this study, the pressure is adjusted so
that the water is varied in the vapor phase and liquid phase (subcritical water). In
hydrothermal carbonization, temperature was varied at 225 °C and 250 °C with
the carbonization time of 5 hours. Chemical activation using KOH as activating
agent was done after obtained the hydrochar from hydrothermal carbonization
process. Produced activated carbons were characterized by nitrogen adsorptiondesorption,
scanning electron microscope, Fourier transform infrared, X-ray
diffraction, and Raman spectroscopy. Electrochemical properties of these carbons
were characterized by cyclic voltammetry, galvanostatic charge-discharge, and
electrochemical impedance spectroscopy. It is found that the largest surface area
of produced activated carbons could be obtained is 2907.31 m2/g and the largest
capacitance of supercapacitor is 15.57 F/g. |
|---|