OPTIMASI PROSES LIOFILISASI DAN KARAKTERISASI LIOFILISAT FORMULA NANOPARTIKEL BERBASIS KITOSAN DAN POLOKSAMER YANG MENGANDUNG ANTISENSE OLIGODEOKSINUKLEOTIDA BERTARGET GEN EBA-175 DAN DHS
Nanoparticles uses for drug delivery system of as-ODN as malaria therapy agent are to prevent enzymatic degradation and to improve as-ODN deliverance to target. Freeze dried is performed to nanoparticles preparation with the purpose is to improve the efficiency of packaging and use of preparation....
Saved in:
| Main Author: | |
|---|---|
| Format: | Final Project |
| Language: | Indonesia |
| Online Access: | https://digilib.itb.ac.id/gdl/view/44139 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Institut Teknologi Bandung |
| Language: | Indonesia |
| Summary: | Nanoparticles uses for drug delivery system of as-ODN as malaria therapy agent are to prevent enzymatic
degradation and to improve as-ODN deliverance to target. Freeze dried is performed to nanoparticles
preparation with the purpose is to improve the efficiency of packaging and use of preparation.
Cryoprotectant is added to nanoparticles to prevent freezing and drying stress while nanoparticles is
performing freeze dry. The purpose of this study is to find the optimum cryoprotectant that could
maintain the particle’s diameter of nanoparticles while freeze dry processing. Optimization of
nanoparticles was performed to mannitol, lactose, glucose, fructose and dextran with 1%, 5%, 10%, 15%
and 20% concentrations. The optimum cryoprotectant was assessed by ratio of nanoparticles diameter
before and after freeze dry, the closer the ratio to 1 the better. The optimum cryoprotectant to protect
freezing and drying stress are 15% lactose and 10% glucose for chitosan nanoparticles formulation and
10% glucose and 10% mannitol for chitosan-poloxamer nanoparticles. Freeze dried chitosan nanoparticles
has diameter particles, polydispersity index and zeta potential: 115,97-246,83 nm, 0,209-0,457, and +7,84
until +26,00 mV respectively. While freeze dried chitosan-poloxamer nanoparticles has diameter particles,
polydispersity index and zeta potential: 161,5-212,7 nm, 0,335-0,451, and -1,80 until +15,40 mV
respectively. Reconstitution time of freeze dried nanoparticles was between 71,5-832,5 seconds. Thermal
analysis showed that there are some new peaks at thermal curve of freeze dried nanoparticles with
cryoprotectant than freeze dried nanoparticles without cryoprotectant. Morphology observation of
freeze dried product with SEM showed the difference between freeze dried nanoparticles before and
after cryoprotectant addition.
|
|---|