Influence of water-to-cement ratio on the compressive strength of cement-biochar-spent ion exchange resins matrix
The influence of water-to-cement ratio (w/c) on the compressive strength of cement-biochar-spent resins matrix was investigated. Spent resins waste from nuclear reactor operation was solidified using cement with w/c ranging from 0.35 to 0.90 by weight. In this study, biochar was used as a cement adm...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit Universiti Kebangsaan Malaysia
2017
|
| Online Access: | http://journalarticle.ukm.my/11391/1/34%20Zalina%20Laili.pdf http://journalarticle.ukm.my/11391/ http://www.ukm.my/jsm/malay_journals/jilid46bil9_2017/KandunganJilid46Bil9_2017.html |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Kebangsaan Malaysia |
| Language: | English |
| Summary: | The influence of water-to-cement ratio (w/c) on the compressive strength of cement-biochar-spent resins matrix was investigated. Spent resins waste from nuclear reactor operation was solidified using cement with w/c ranging from 0.35 to 0.90 by weight. In this study, biochar was used as a cement admixture. Some properties of spent resins and biochar were determined prior to the formulation study. Compressive strength of harden cement-biochar-spent resins matrix was determined at 28 days. The compressive strength of cement-biochar-spent resins matrix was found to depend on the w/c and the amount of spent resins added to the formulation. The immersion test of cement-biochar-spent resins matrix showed no significant effects of cracking and swelling. The compressive strength of the cement-biochar-spent resins matrix increased after two weeks in water immersion test. |
|---|