The digitalisation in cobalt-chromium framework fabrication. Surface roughness analysis : a pilot study
Selective laser melting (SLM) is a new technique in fabricating cobalt-chromium denture framework. However, the surface properties of cobalt-chromium denture framework fabricated using the aforementioned technique have not been widely investigated. The aim of this paper was to investigate the surfac...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit Universiti Kebangsaan Malaysia
2021
|
| Online Access: | http://journalarticle.ukm.my/18176/1/18.pdf http://journalarticle.ukm.my/18176/ https://www.ukm.my/jsm/malay_journals/jilid50bil10_2021/KandunganJilid50Bil10_2021.html |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Kebangsaan Malaysia |
| Language: | English |
| Summary: | Selective laser melting (SLM) is a new technique in fabricating cobalt-chromium denture framework. However, the surface properties of cobalt-chromium denture framework fabricated using the aforementioned technique have not been widely investigated. The aim of this paper was to investigate the surface roughness of cobalt-chromium alloy in removable partial denture fabricated with SLM technique. Cobalt-chromium denture frameworks were fabricated with two techniques (n = 10); the conventional lost-wax casting (conventional group) and SLM techniques (SLM group). Specimens from the conventional group were subjected to the standard cobalt-chromium denture polishing protocols. No treatment was employed for specimens from the SLM group. All specimens were subjected to surface roughness measurement on polished and fitting surfaces using non-contact optical three-dimensional metrology and surface roughness analysis machine (Infinite Focus Real 3D Alicona). Statistical analysis showed no significant difference in surface roughness between the specimens from conventional and SLM groups (p > 0.05). There was no statistically significant difference in surface roughness between the polished and fitting surfaces of SLM specimens (p > 0.05). Surface roughness quality of the cobalt-chromium denture framework fabricated with the SLM technique is comparable to that fabricated with the conventional lost-wax casting technique. The surface roughness of SLM fabricated cobalt-chromium denture frameworks carries the same surface roughness quality between the polished and fitting surfaces. |
|---|