Effect of aluminium hydroxide loading on the compression stress and modulus, thermal conductivity and acoustic properties of palm-based polyurethane hybrid composite
The effect of adding aluminum hydroxide (ATH) in the palm-based polyurethane hybrid composite was studied. The compression stress and modulus, thermal conductivity and acoustic property were determined. The hybrid composite was prepared by adding 10 wt% of oil palm empty fruit bunch fibre (EFB) foll...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Kebangsaan Malaysia
2011
|
| Online Access: | http://journalarticle.ukm.my/2404/1/15_Nor.pdf http://journalarticle.ukm.my/2404/ http://www.ukm.my/jsm/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Kebangsaan Malaysia |
| Language: | English |
| Summary: | The effect of adding aluminum hydroxide (ATH) in the palm-based polyurethane hybrid composite was studied. The compression stress and modulus, thermal conductivity and acoustic property were determined. The hybrid composite was prepared by adding 10 wt% of oil palm empty fruit bunch fibre (EFB) followed by ATH at varying amount of 2, 4 and 6 wt% of the overall mass of the resin. The compression stress and modulus gave the highest values of 575 kPa and 2301 kPa, respectively at 2 wt% ATH. At 4 wt% ATH, the compression stress and modulus decreased to 431 kPa and 1659 kPa, respectively and further decreased at 6 wt% ATH to 339 kPa and 1468 kPa respectively. The k-value increased with the increment of the ATH loading exhibited a poor thermal conductivity. Sound absorption analysis indicated that the absorption coefficient was higher at higher frequency (4000 Hz) for all samples with PU-EFB/ATH with 4% ATH showed the highest absorption coefficient. |
|---|