Investigation on the thermal properties, density and degradation of quaternary iron and titanium phosphate based glasses

• Main Authors: Syed Shaharuddin, Sharifah Imihezri, Ahmed, Ifty, Furniss, David, Parsons, Andrew James, Rudd, Christopher Douglas
• Format: Conference or Workshop Item
• Language: English; English; English
• Published: IOP Publishing 2016
• Subjects: T Technology (General)
• Online Access: http://irep.iium.edu.my/93233/1/93233_Investigation%20on%20the%20thermal%20properties.pdf; http://irep.iium.edu.my/93233/2/93233_Investigation%20on%20the%20thermal%20properties_WoS.pdf; http://irep.iium.edu.my/93233/3/93233_Investigation%20on%20the%20thermal%20properties_SCOPUS.pdf; http://irep.iium.edu.my/93233/; https://iopscience.iop.org/article/10.1088/1757-899X/114/1/012124
• Institution: Universiti Islam Antarabangsa Malaysia

The possibility of producing phosphate based glasses (PBG) with tailored degradation profile allows for unique utilisation in biomedical application. Various compositions in the phosphate based glass (PBG) system of (50-x)P2O5-40Ca-(5+x)Na-5TiO2 and (50-x)P2O5-40Ca-(5+x)Na-5Fe2O3, where x= 5 and 10 were prepared and characterised. Method as differential scanning calorimetry (DSC) has been used to characterise the thermal properties of these phosphate based glasses. It was observed that both glass transition temperature (Tg) and onset of crystalisatisation temperature (Tx) increased with increasing phosphate content. In addition, Tg values were found to be higher for the P2O5-CaO-Na2O-TiO2 glass system compared to P2O5-CaO-Na2O-Fe2O3 glass system. The density result showed that increasing the P2O5 content at the expense Na2O led to a decrease in density for both glass systems. The dissolution study of these glasses was conducted in phosphate buffered saline (PBS). It was observed that the dissolution rate of P2O5-CaO-Na2O-Fe2O3 glass system was higher than the P2O5-CaO-Na2O-TiO2 glass system. The dissolution rate for both glass systems was in the order of 10-6 g cm-2 hr-1 .