Effects of LiC104 and EC on the ENR 50 for electrochemical system / Nurul Raihan Mohd Suib

• Main Author: Mohd Suib, Nurul Raihan
• Format: Student Project
• Language: English
• Published: 2006
• Subjects: Electricity and magnetism; Analytical chemistry
• Online Access: https://ir.uitm.edu.my/id/eprint/46371/1/46371.pdf; https://ir.uitm.edu.my/id/eprint/46371/
• Institution: Universiti Teknologi Mara

In this study, Epoxidized Natural Rubber (ENR-50) was used as a host polymer. ENR-50, ethylene carbonate (EC) and inorganic lithium perchlorate (LiC104) were mixed in the desired proportions and dissolved in 30ml of tetrahydrofuran (THF) solution. The solutions were then poured into various Petri dishes and left to form the film at room temperature. EC was used as a plasticizer. The electrical conductivity of all samples was calculated using the bulk resistance value obtained from the complex impedance plot in the frequency range between 100Hz and 1MHz. The highest electrical conductivity obtained for the salted film containing lithium perchlorate is 8.55xlO"sS/cm at room temperature. The plot of conductivity versus wt percent of salt indicates that the conductivity increase with increasing dopant content up to amount of 30wt percent for lithium perchlorate. The highest conducting plasticize polymer electrolyte complex with 30wt percent EC has the highest conductivity value of l.lxlO^S/cm. The highest conducting film for the plasticized ENR-50 was then used as an electrolyte in the fabrication of lithium-air cell. The discharge capacity obtained from the cell is 574mAhg"1.