Low-velocity impact damage of woven fabric composites: Finite element simulation and experimental verification
This paper addresses the response of Glass Fiber Reinforced Plastic laminates (GFRPs) under low-velocity impact. Experimental tests were performed according to ASTM: D5628 for different initial impact energy levels ranging from 9.8 J to 29.4 J and specimen thicknesses of 2, 3 and 4 mm. The impact da...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Published: |
Elsevier
2014
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/11811/ http://doi.org/10.1016/j.matdes.2013.07.068 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Malaya |
| Summary: | This paper addresses the response of Glass Fiber Reinforced Plastic laminates (GFRPs) under low-velocity impact. Experimental tests were performed according to ASTM: D5628 for different initial impact energy levels ranging from 9.8 J to 29.4 J and specimen thicknesses of 2, 3 and 4 mm. The impact damage process and contact stiffness were studied incrementally until a perforation phase of the layered compounds occurred, in line with a force–deflection diagram and imaging of impacted laminates. The influence that impact parameters such as velocity and initial energy had on deflection and damage of the test specimens was investigated. Finite Element Simulation (FES) was done using MSC. MARC® was additionally carried out to understand the impact mechanism and correlation between these parameters and the induced damage. The simulation and experimental results reached good accord regarding maximum contact force and contact time with insignificant amount of damage. |
|---|