Synthesis and characterization of nanostructured Co-Pt magnetic films electrodeposited from tartrate-stabilized chloride baths
Cobalt-platinum (Co-Pt) nanocrystalline alloy thin films were electrodeposited on brass substrates using a novel stable single bath system containing ammonium tartrate and ammonia solution as complex forming additive. The as-synthesized Co-Pt films were then subjected to various chemical, micro-st...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/15632/1/0001.pdf http://eprints.um.edu.my/15632/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Malaya |
| Language: | English |
| Summary: | Cobalt-platinum (Co-Pt) nanocrystalline alloy thin films were electrodeposited on brass substrates
using a novel stable single bath system containing ammonium tartrate and ammonia solution as complex
forming additive. The as-synthesized Co-Pt films were then subjected to various chemical, micro-structural,
nano-structural and magnetic characterizations. Energy dispersive X-ray spectroscopy (EDS) analysis showed
that the compositions of the electrodeposits could be controlled by adjusting the metal ions ratio in the
electrolytic bath and by varying the current density. X-ray diffraction (XRD) results showed that the asdeposited
films with nanocrystalline structure contained face-center cubic (fcc) CoPt3 phase. Calculation of
crystallite size from X-ray peak broadening showed that the crystallite sizes were in nanoscale dimension.
Scanning electron microscopy (SEM) results showed formation of granules and clusters. Atomic force
microscopy (AFM) and infinite focus microscopy (IFM) results showed granular surface morphology and
approximately similar surface roughness value on C043-Pt57 film. Magnetic force microscopy (MFM)
characterization on C043-Pt57showed existence of correlation between magnetic force and surface topography. The saturation magnetization (Ms) values of as-synthesized nanostructured Co-Pt thin films increased with increasing of Co content. |
|---|