Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy

This paper presents an experimental study of surface integrity in end milling of Hastelloy C-2000. The experiment was carried out using two different cutting inserts under wet conditions – namely physical vapor deposition coated carbide with TiAlN and uncoated carbide. Design of experiment was imple...

Full description

Saved in:
Bibliographic Details
Main Authors: Norhaida, Ab Razak, Md Mustafizur, Rahman, Kadirgama, Kumaran
Format: Article
Language:English
Published: Universiti Malaysia Pahang 2014
Subjects:
Online Access:http://umpir.ump.edu.my/id/eprint/8175/1/8_Razak_et_al.pdf
http://umpir.ump.edu.my/id/eprint/8175/
http://dx.doi.org/10.15282/ijame.9.2013.8.0130
http://dx.doi.org/10.15282/ijame.9.2013.8.0130
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Universiti Malaysia Pahang
Language: English
id my.ump.umpir.8175
record_format eprints
spelling my.ump.umpir.81752023-08-22T02:04:30Z http://umpir.ump.edu.my/id/eprint/8175/ Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy Norhaida, Ab Razak Md Mustafizur, Rahman Kadirgama, Kumaran TJ Mechanical engineering and machinery This paper presents an experimental study of surface integrity in end milling of Hastelloy C-2000. The experiment was carried out using two different cutting inserts under wet conditions – namely physical vapor deposition coated carbide with TiAlN and uncoated carbide. Design of experiment was implemented with a Box-Behnken design. The surface integrity of the workpiece was analyzed through scanning electron microscopy (SEM) and chemical element changes were inspected by an energy dispersive X-ray (EDX) test. The surface integrity of Hastelloy C-2000 was better when machining with coated carbide compared to uncoated carbide cutting inserts, mainly because the coating layer of coated carbide acted as a protecting layer to the cutting tool insert. Surface defects such as feed marks, surface tearing, plucking, cracking and adhered chips were found during the machining process. The chemical element changes happened due to the adhesion and diffusion mechanisms which were identified using SEM and EDX. Universiti Malaysia Pahang 2014-06-30 Article PeerReviewed application/pdf en cc_by http://umpir.ump.edu.my/id/eprint/8175/1/8_Razak_et_al.pdf Norhaida, Ab Razak and Md Mustafizur, Rahman and Kadirgama, Kumaran (2014) Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy. International Journal of Automotive and Mechanical Engineering (IJAME), 9 (1). pp. 1578-1587. ISSN 1985-9325(Print); 2180-1606 (Online). (Published) http://dx.doi.org/10.15282/ijame.9.2013.8.0130 http://dx.doi.org/10.15282/ijame.9.2013.8.0130
institution Universiti Malaysia Pahang
building UMP Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Malaysia Pahang
content_source UMP Institutional Repository
url_provider http://umpir.ump.edu.my/
language English
topic TJ Mechanical engineering and machinery
spellingShingle TJ Mechanical engineering and machinery
Norhaida, Ab Razak
Md Mustafizur, Rahman
Kadirgama, Kumaran
Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
description This paper presents an experimental study of surface integrity in end milling of Hastelloy C-2000. The experiment was carried out using two different cutting inserts under wet conditions – namely physical vapor deposition coated carbide with TiAlN and uncoated carbide. Design of experiment was implemented with a Box-Behnken design. The surface integrity of the workpiece was analyzed through scanning electron microscopy (SEM) and chemical element changes were inspected by an energy dispersive X-ray (EDX) test. The surface integrity of Hastelloy C-2000 was better when machining with coated carbide compared to uncoated carbide cutting inserts, mainly because the coating layer of coated carbide acted as a protecting layer to the cutting tool insert. Surface defects such as feed marks, surface tearing, plucking, cracking and adhered chips were found during the machining process. The chemical element changes happened due to the adhesion and diffusion mechanisms which were identified using SEM and EDX.
format Article
author Norhaida, Ab Razak
Md Mustafizur, Rahman
Kadirgama, Kumaran
author_facet Norhaida, Ab Razak
Md Mustafizur, Rahman
Kadirgama, Kumaran
author_sort Norhaida, Ab Razak
title Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
title_short Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
title_full Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
title_fullStr Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
title_full_unstemmed Experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
title_sort experimental study on surface integrity in end milling of hastelloy c-2000 superalloy
publisher Universiti Malaysia Pahang
publishDate 2014
url http://umpir.ump.edu.my/id/eprint/8175/1/8_Razak_et_al.pdf
http://umpir.ump.edu.my/id/eprint/8175/
http://dx.doi.org/10.15282/ijame.9.2013.8.0130
http://dx.doi.org/10.15282/ijame.9.2013.8.0130
_version_ 1775622220645662720