Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution
Access is limited to UniMAP community.
Saved in:
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Learning Object |
| Language: | English |
| Published: |
Universiti Malaysia Perlis
2012
|
| Subjects: | |
| Online Access: | http://dspace.unimap.edu.my/xmlui/handle/123456789/20826 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Malaysia Perlis |
| Language: | English |
| id |
my.unimap-20826 |
|---|---|
| record_format |
dspace |
| spelling |
my.unimap-208262012-09-05T08:55:31Z Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution Mohd Firdaus, Jaafar Dr. Haftirman Stress corrosion cracking (SCC) Brittle cracks Austenitic stainless steel Sodium choride (NaCI) Access is limited to UniMAP community. Stress corrosion cracking is the formation of brittle cracks in a normally sound material through the simultaneous action of a tensile stress and a corrosive environment. Stress corrosion cracking occurs when there have stress applied and chemical reaction to the samples. There have two types of cracking which intergranular and transgranular morphology. Mechanical properties of these specimens are investigated by using tensile test. This test is conducted by Universal Testing Machine (UTM). Specimens are immersed in 3.5 wt % NaCl for variety times which 10, 200, 400, 600, 800, 1000, and 1200 hours because to make data comparison. Microstructure analysis is conducted by using Scanning Electron Microscopy and Smile View software to determine the crack propagation on the specimen’s surface. Graph Crack lines vs Time was plotted to show the comparison when immersed in 3.5 wt % NaCl for variety time. 2012-09-05T08:55:31Z 2012-09-05T08:55:31Z 2009-04 Learning Object http://hdl.handle.net/123456789/20826 en Universiti Malaysia Perlis School of Mechatronic Engineering |
| institution |
Universiti Malaysia Perlis |
| building |
UniMAP Library |
| collection |
Institutional Repository |
| continent |
Asia |
| country |
Malaysia |
| content_provider |
Universiti Malaysia Perlis |
| content_source |
UniMAP Library Digital Repository |
| url_provider |
http://dspace.unimap.edu.my/ |
| language |
English |
| topic |
Stress corrosion cracking (SCC) Brittle cracks Austenitic stainless steel Sodium choride (NaCI) |
| spellingShingle |
Stress corrosion cracking (SCC) Brittle cracks Austenitic stainless steel Sodium choride (NaCI) Mohd Firdaus, Jaafar Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| description |
Access is limited to UniMAP community. |
| author2 |
Dr. Haftirman |
| author_facet |
Dr. Haftirman Mohd Firdaus, Jaafar |
| format |
Learning Object |
| author |
Mohd Firdaus, Jaafar |
| author_sort |
Mohd Firdaus, Jaafar |
| title |
Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| title_short |
Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| title_full |
Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| title_fullStr |
Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| title_full_unstemmed |
Stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (NaCI) solution |
| title_sort |
stress corrosion cracking behavior of austenitic stainless steel in 3.5 wt % sodium chloride (naci) solution |
| publisher |
Universiti Malaysia Perlis |
| publishDate |
2012 |
| url |
http://dspace.unimap.edu.my/xmlui/handle/123456789/20826 |
| _version_ |
1643791124120207360 |