Failure investigation on reheater tube due to deposit and wall thinning

• Main Authors: Purbolaksono J., Tarlochan F., Rahman M.M., Nordin N.F., Ahmad B.
• Other Authors: 8621252500
• Format: Article
• Published: 2023
• Subjects: Boiler material; Deposits; Failure analysis; High temperature; Thinning; Tube burst; Boiler deposits; Boilers; Corrosion; Microscopic examination; Safety factor; Scale (deposits); Tubes (components); Dimensional measurements; Failure investigation; Finite element modeling; Inner tubes; Reheater tubes; Root cause; Scale formation; Wall thinning; Quality assurance
• Institution: Universiti Tenaga Nasional

Failure analysis of a reheater tube showed that the failure was caused by overheating and wall thinning. Finite element modeling, dimensional measurements, and microscopic examinations were performed to investigate the root cause of the failure. Wall thinning, due to excessive coal-ash corrosion, an...