Investigating the specific absorption rate and antimicrobial activity of Mn0.25Fe2.75O4/Ag ferrogel based on carboxymethyl cellulose/polyvinyl alcohol composite polymer

Investigating the specific absorption rate and antimicrobial activity of Mn0.25Fe2.75O4/Ag ferrogel based on carboxymethyl cellulose/polyvinyl alcohol composite polymer

Carboxymethyl cellulose (CMC)/polyvinyl alcohol (PVA)-Mn0.25Fe2,75O4/Ag ferrogels was fabricated by using the freezing-thawing method. Mn0.25Fe2.75O4/Ag magnetic fillers of ferrogels were synthesized by using coprecipitation and chemical reduction methods. Characterization of Mn0.25Fe2.75O4/Ag nanop...

Full description

Saved in:
Bibliographic Details
Main Authors: Sunaryono, Sunaryono, Nadiya Miftachul Chusna, Nadiya Miftachul Chusna, Muchlis Fajar Hidayat, Muchlis Fajar Hidayat, Andy Choerullah, Andy Choerullah, Samsul Hidayat, Samsul Hidayat, Nandang Mufti, Nandang Mufti, Aripriharta, Aripriharta, Arif Nur Afandi, Arif Nur Afandi, Juniastel Rajagukguk, Juniastel Rajagukguk, Nik Malek, Nik Ahmad Nizam, Ahmad Taufiq, Ahmad Taufiq
Format: Article
Published: SAGE Publications Ltd 2023
Subjects:
Q Science (General)
Online Access:http://eprints.utm.my/104925/
http://dx.doi.org/10.1177/08927057231167419
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Universiti Teknologi Malaysia
Description
Summary:Carboxymethyl cellulose (CMC)/polyvinyl alcohol (PVA)-Mn0.25Fe2,75O4/Ag ferrogels was fabricated by using the freezing-thawing method. Mn0.25Fe2.75O4/Ag magnetic fillers of ferrogels were synthesized by using coprecipitation and chemical reduction methods. Characterization of Mn0.25Fe2.75O4/Ag nanopowders was carried out using X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM), Vibrating Sample Magnetometer (VSM) instrument, and antimicrobial activity. At the same time, CMC/PVA-Mn0.25Fe2.75O4/Ag ferrogels were characterized by using magnetothermal instrument. The XRD pattern of the magnetite filler shows the peaks by the Fe3O4 and Ag phases, respectively. The TEM image, there are Mn0.25Fe2.75O4 and Ag with particle size distributions of 5–7 and 10–13 nm, respectively. The hysterical curve from VSM characterization shows a decrease in the value of magnetization saturation from 16.9 to 14.7 emu/g along with the addition of Ag material. Antimicrobial activity was tested using the agar diffusion method. Mn0.25Fe2.75O4/Ag samples showed very good results indicated by the widening of the zone of inhibition around the sample. Thus, CMC/PVA-Mn0.25Fe2.75O4/Ag ferrogels has the potential application to be applied in hyperthermia therapy as well as antimicrobial materials.