The influence of SS316l foam fabrication parameter using powder metallurgy route
Metal foams are widely produced by using different techniques such as compaction and replication method. In this study, slurry method also known as replication method has been used to produce SS316L foams. SS316L powders (50wt% and 60wt%) were mixed with the binders and distilled water by using mech...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Conference or Workshop Item |
Published: |
2014
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/68568/ http://www.ttp.net/978-3-03835-149-8.html |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Universiti Teknologi Malaysia |
id |
my.utm.68568 |
---|---|
record_format |
eprints |
spelling |
my.utm.685682017-10-08T03:31:22Z http://eprints.utm.my/id/eprint/68568/ The influence of SS316l foam fabrication parameter using powder metallurgy route Mad Rosip, N. I. Ahmad, Sufizar Jamaluddin, Khairur Rijal Mat Nor, F. T Technology (General) Metal foams are widely produced by using different techniques such as compaction and replication method. In this study, slurry method also known as replication method has been used to produce SS316L foams. SS316L powders (50wt% and 60wt%) were mixed with the binders and distilled water by using mechanical stirrer. Polyethylene Glycol (PEG) and Carboxyl Methyl Cellulose (CMC) were used as binders. Polyurethane (PU) foam was used as scaffold and dipped into SS316L slurry then dried in room temperature for 24 hours. Sintering process has been done in two different temperatures which were 1200oC and 1300oC in vacuum furnace. The morphological study was performed using Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray (EDX). The SEM micrograph showed that the cells were interconnected and the structures become denser as the sintering temperature increase. The average pores size is ranging from 252.8 μm-353.8 μm, while strut size ranging from 50.2 μm -79.9 μm based on SEM micrograph analysis. The elemental analysis from EDX showed the element presence in the SS316L foam remain from SS316L powder which are Chromium (Cr), Nickel (Ni), Molybdenum (Mo), Cooper (Cu), Nitrogen (N2), Sulphur (S) and Silicon (Si). Higher sintering temperature contributes better grain growth between particles where the point-contact between the particles expanded and disappear the small pores. 2014 Conference or Workshop Item PeerReviewed Mad Rosip, N. I. and Ahmad, Sufizar and Jamaluddin, Khairur Rijal and Mat Nor, F. (2014) The influence of SS316l foam fabrication parameter using powder metallurgy route. In: 5th International Conference on Material and Manufacturing Technology, ICMMT 2014, 8-9 May, 2014, Kuala Lumpur, Malaysia. http://www.ttp.net/978-3-03835-149-8.html |
institution |
Universiti Teknologi Malaysia |
building |
UTM Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Teknologi Malaysia |
content_source |
UTM Institutional Repository |
url_provider |
http://eprints.utm.my/ |
topic |
T Technology (General) |
spellingShingle |
T Technology (General) Mad Rosip, N. I. Ahmad, Sufizar Jamaluddin, Khairur Rijal Mat Nor, F. The influence of SS316l foam fabrication parameter using powder metallurgy route |
description |
Metal foams are widely produced by using different techniques such as compaction and replication method. In this study, slurry method also known as replication method has been used to produce SS316L foams. SS316L powders (50wt% and 60wt%) were mixed with the binders and distilled water by using mechanical stirrer. Polyethylene Glycol (PEG) and Carboxyl Methyl Cellulose (CMC) were used as binders. Polyurethane (PU) foam was used as scaffold and dipped into SS316L slurry then dried in room temperature for 24 hours. Sintering process has been done in two different temperatures which were 1200oC and 1300oC in vacuum furnace. The morphological study was performed using Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray (EDX). The SEM micrograph showed that the cells were interconnected and the structures become denser as the sintering temperature increase. The average pores size is ranging from 252.8 μm-353.8 μm, while strut size ranging from 50.2 μm -79.9 μm based on SEM micrograph analysis. The elemental analysis from EDX showed the element presence in the SS316L foam remain from SS316L powder which are Chromium (Cr), Nickel (Ni), Molybdenum (Mo), Cooper (Cu), Nitrogen (N2), Sulphur (S) and Silicon (Si). Higher sintering temperature contributes better grain growth between particles where the point-contact between the particles expanded and disappear the small pores. |
format |
Conference or Workshop Item |
author |
Mad Rosip, N. I. Ahmad, Sufizar Jamaluddin, Khairur Rijal Mat Nor, F. |
author_facet |
Mad Rosip, N. I. Ahmad, Sufizar Jamaluddin, Khairur Rijal Mat Nor, F. |
author_sort |
Mad Rosip, N. I. |
title |
The influence of SS316l foam fabrication parameter using powder metallurgy route |
title_short |
The influence of SS316l foam fabrication parameter using powder metallurgy route |
title_full |
The influence of SS316l foam fabrication parameter using powder metallurgy route |
title_fullStr |
The influence of SS316l foam fabrication parameter using powder metallurgy route |
title_full_unstemmed |
The influence of SS316l foam fabrication parameter using powder metallurgy route |
title_sort |
influence of ss316l foam fabrication parameter using powder metallurgy route |
publishDate |
2014 |
url |
http://eprints.utm.my/id/eprint/68568/ http://www.ttp.net/978-3-03835-149-8.html |
_version_ |
1643655961538199552 |