Effects of the partial substitution of tin (Sn) into the strontium (Sr) site of the high-Tc BSCCO system

The effects of the partial substitution of Tin (Sn) into the Strontium (Sr) site of the high-Tc BSCCO system is studied. X-ray diffraction analysis revealed the co-existence of the high-Tc and low-Tc phases in most of the samples. Electrical resistivity measurements showed zero resistivity at 115 K...

Full description

Saved in:
Bibliographic Details
Main Author: Vallente, Amancia Ragandac
Format: text
Language:English
Published: Animo Repository 1997
Subjects:
Tin
Online Access:https://animorepository.dlsu.edu.ph/etd_masteral/1819
https://animorepository.dlsu.edu.ph/cgi/viewcontent.cgi?article=8657&context=etd_masteral
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: De La Salle University
Language: English
Description
Summary:The effects of the partial substitution of Tin (Sn) into the Strontium (Sr) site of the high-Tc BSCCO system is studied. X-ray diffraction analysis revealed the co-existence of the high-Tc and low-Tc phases in most of the samples. Electrical resistivity measurements showed zero resistivity at 115 K for the sample prepared via solid-state reaction method and with nominal composition of Bi2(Sr1.7Sn0.3)Ca2Cu3)16. Susceptibility measurement of this sample showed a transition onset of about 112 K. Scanning Electron Microscopy analysis of this sample revealed that bar-shaped crystals were formed.