Controlled Release ot Methvl Salicvlate in ChitosanPoli[N-Isopropvlacrvlamide] Semi-Interpenetrating Networks
A semi-interpenetrating network (semi-IPN) was produced by polymerizing Nisopropylacrylamide (NIP AAm) in the presence of chitosan and cross-linking agent, ethylene glycol dimethacrylate (EGDMA). The resulting material did not swell as much as poly(N-isopropylacrylamide) (piPAAm), but still showed t...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | text |
| Published: |
Archīum Ateneo
2010
|
| Subjects: | |
| Online Access: | https://archium.ateneo.edu/chemistry-faculty-pubs/91 https://archium.ateneo.edu/cgi/viewcontent.cgi?article=1090&context=chemistry-faculty-pubs |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Ateneo De Manila University |
| Summary: | A semi-interpenetrating network (semi-IPN) was produced by polymerizing Nisopropylacrylamide (NIP AAm) in the presence of chitosan and cross-linking agent, ethylene glycol dimethacrylate (EGDMA). The resulting material did not swell as much as poly(N-isopropylacrylamide) (piPAAm), but still showed temperature- and pHresponsiveness. Swelling and differential scanning calorimetry (DSC) experiments showed that the lower critical solution temperature (LCST) of the material was at 31 °C. The semiIPN was swollen below 30 °C but started to collapse at this temperature. This is in the same range as the LCST of carrageenan-piPAAm semi-IPN. The chitosan-piPAAm semi-IPN was in a collapsed state and reached maximum swelling at pH 9 whereas pure piP AAm and pure chitosan both became swollen at a lower pH. Methyl salicylate was absorbed by the semi-IPN. Its release was monitored with respect to temperature. The temperature-responsive release of methyl salicylate was more pronounced at the LCST of31° C. |
|---|