Fatigue crack growth studies on welded joints with multiple weld toe cracks

Fatigue crack growth studies on welded joints with multiple weld toe cracks

This PhD study examines fatigue crack growth analysis and testing case studies of multiple surface cracks for assessing fatigue cracks propagation life of welded joints with surface cracks at weld toe regions. Fatigue analysis was performed based on fracture mechanics concepts using the crack propag...

Saved in:

書目詳細資料
主要作者:	Tsang, Kin Shun
其他作者:	Pang Hock Lye, John
格式:	Thesis-Doctor of Philosophy
語言:	English
出版:	Nanyang Technological University 2021
主題:	Engineering::Mechanical engineering
在線閱讀:	https://hdl.handle.net/10356/153419
標簽:	添加標簽沒有標簽, 成為第一個標記此記錄!

相似書籍

Fatigue cumulative damage and crack propagation analysis of welded joints
由: Shi, Zhao Feng.
出版: (2009)

Influence of weld toe radii on fatigue life prediction
由: Pang, John Hock Lye, et al.
出版: (2018)

Fatigue failure investigation on offshore pipelines with 3D cracks at the welding joints
由: Yoon, Sang Ryun
出版: (2023)

Mode mixity for tubular K-joints with weld toe cracks
由: Qian, X., et al.
出版: (2014)

Structural Health Monitoring (SHM) of fatigue crack growth in welded joints
由: Tan, Yong Quan.
出版: (2013)

Prediction of weld toe magnification factors for semi-elliptical cracks in double T-butt joints
由: Lim, Wee Fong.
出版: (2013)

Prediction of weld toe magnification factors for semi-elliptical cracks in single T-butt joints
由: Hoon, Deborah Jun-Min.
出版: (2013)

Simulation of 3D fatigue crack propogation in welded T-joints
由: Sun, Shangqing.
出版: (2008)

Prediction of stress intensity magnification factors of a semi-elliptical weld toe crack in load-carrying cruciform fillet-welded joints
由: Wai, Myo Htet
出版: (2017)

Mode mixity for circular hollow section X joints with weld toe cracks
由: Qian, X., et al.
出版: (2014)

Prediction of weld toe magnification factors for semi-elliptical cracks in X-joints under bending loading
由: Akbar Ali, Esmah Kamarudeen
出版: (2014)

Structural fatigue investigation of transverse surface crack growth in rail steels and thermite welds subjected to in-plane and out-of-plane loading
由: Liu, Yang, et al.
出版: (2022)

Fatigue crack growth studies for multiple surface cracks
由: Tum, Jierong
出版: (2014)

Prediction of weld toe magnification factors for semi-elliptical cracks in single T-butt joints under bending loading
由: Sivakumaran Balachandran
出版: (2014)

Prediction of weld toe magnification factor for semi-elliptical cracks in double T-butt joints under bending loading
由: Boyani, Geetha Sharanya
出版: (2014)

Fatigue analysis of welded joints
由: Lim, Jonathan Chung Ying
出版: (2019)

Fatigue analysis of welded joints
由: Koh, Jackson Wen Qiang
出版: (2019)

Monitoring fatigue crack growth in welded joints using alternating current potential drop (ACPD) technique
由: Lie, Seng Tjhen.
出版: (2008)

Failure analysis of two 3D embedded cracks in offshore pipelines at the welding joints
由: Hoo, Zhiong Sheng
出版: (2022)

Numerical investigation on crack growth in girth welded pipeline under various loadings
由: Chia, Chi Yong
出版: (2015)

Fracture analysis of load-carrying cruciform fillet welded joints with multiple cracks
由: Lie, Seng-Tjhen, et al.
出版: (2019)

Application of Hybrid Transient Thermal Tensioning/Trailing Active Cooling Treatment for Minimizing Distortion, Residual Stress, and Fatigue Crack Growth Rate of Friction Stir Welding Joints
由: Ilman, Mochammad Noer, et al.
出版: (2022)

Failure Assessment Diagram (FAD) analysis of fatigue test results for X65 welded joints
由: Hoh, Hsin Jen, et al.
出版: (2018)

An eta-approach to evaluate the elastic-plastic energy release rate for weld-toe cracks in tubular K-joints
由: Zhang, Y., et al.
出版: (2014)

Multi-crack dynamic interaction effect on oil and gas pipeline weld joints based on VCCT
由: Cui, Wei, et al.
出版: (2022)

Fatigue assessment of cracked pipes with weld misalignment by using stress intensity factors
由: Zhao, Hai-Sheng, et al.
出版: (2020)

Fatigue crack growth modelling and analysis
由: Wong, Brian Sixian
出版: (2018)

Ultimate strength and fracture behaviour of cracked welded square hollow section T-joints
由: Yang, Zhengmao
出版: (2008)

Mechanisms of cracking in laser welding of magnesium alloy AZ91D
由: Zhou, Wei, et al.
出版: (2022)

Modelling fatigue crack growth behaviour of a surface crack in rail steel
由: Kwok, Yan Ting
出版: (2019)

Modeling the crack interference in X80 oil and gas pipeline weld
由: Cui, Wei, et al.
出版: (2023)

Root cracking in tubular joints with enhanced partial joint penetration welds
由: Marshall, P.W., et al.
出版: (2014)

Root cracking in tubular joints with enhanced partial joint penetration welds
由: Marshall, P.W., et al.
出版: (2014)

Online monitoring of fatigue damage in welded joints using diffuse ultrasound
由: Gao, Shuling, et al.
出版: (2024)

Fracture assessment of cracked clad pipelines with weld misalignment
由: Zhao, Haisheng
出版: (2018)

Fatigue failure investigation in MRT rails with an internal crack
由: Cheong, Xiang Shun
出版: (2019)

Numerical simulation for fatigue crack propagation in steel beams with welded transverse stiffeners
由: Wanchalerm Triamlumlerd
出版: (2015)

Behaviour of reinforced welded tubular joints
由: Wong, Looi Kian.
出版: (2009)

Fatigue crack growth investigation on offshore pipelines with three-dimensional interacting cracks
由: Zhang, Yanmei, et al.
出版: (2018)

EFFECT OF WELD-TOE GRINDING ON FATIGUE LIFE BASED ON THEORY OF CRITICAL DISTANCE
由: XU JIAJIA
出版: (2024)