The formation mechanism of metal-ceramic interlayer interface during laser powder bed fusion

Experiments on Laser powder bed fusion (LPBF) of powdered Ti on Al2O3 substrate were conducted and the interface formation was studied using a multi-material fluid dynamics model. Results show that the melt pool is relatively shallow, with relatively flat interlayer interface under LPBF’s conduction...

Full description

Saved in:
Bibliographic Details
Main Authors: Yao, Liming, Xiao, Zhongmin, Huang, Sheng, Ramamurty, Upadrasta
Other Authors: School of Mechanical and Aerospace Engineering
Format: Article
Language:English
Published: 2024
Subjects:
Online Access:https://hdl.handle.net/10356/174328
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Nanyang Technological University
Language: English
Description
Summary:Experiments on Laser powder bed fusion (LPBF) of powdered Ti on Al2O3 substrate were conducted and the interface formation was studied using a multi-material fluid dynamics model. Results show that the melt pool is relatively shallow, with relatively flat interlayer interface under LPBF’s conduction mode. In this condition, a thin sheath of molten Al2O3 forms and acts as a lubricating film for the molten Ti, leading to Rayleigh instability due to high flow inertia. Keyhole formation penetrates the Al2O3 substrate, resulting in a wavy interlayer interface. The recoil pressure from the keyhole and overall melt inertia are suppressed by the highly viscous molten Al2O3, thereby improving single-track melt pool stability. However, the thermal expansion coefficient difference between Ti and Al2O3 led to the formation of transverse cracks. Achieving a defect-free metal-on-ceramic single track remains a challenge, despite this study serving as a guide for melt track and interface control.