The study on the effect of plasticizer on the properties of PVDF films
A systematic study was carried out to investigate the effect of plasticizers on the properties of Polyvinylidene fluoride (PVDF) thin films. PVDF thin films of concentrations 5 wt% and 10 wt% were fabricated and it was observed that N, N Dimethylformamide (DMF) solution is able to completely dissolv...
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| مؤلفون آخرون: | |
| التنسيق: | Final Year Project |
| اللغة: | English |
| منشور في: |
2011
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://hdl.handle.net/10356/44352 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Nanyang Technological University |
| اللغة: | English |
| الملخص: | A systematic study was carried out to investigate the effect of plasticizers on the properties of Polyvinylidene fluoride (PVDF) thin films. PVDF thin films of concentrations 5 wt% and 10 wt% were fabricated and it was observed that N, N Dimethylformamide (DMF) solution is able to completely dissolve a 5 wt% solution of PVDF after magnetic stirring for 24 hours but is unable to dissolve a 10 wt% solution. Ethylene Carbonate (EC) was added to the PVDF-DMF mixture as a plasticizer and was found to be effective in dissolving the PVDF powder. Characterization of the fabricated films with varying ratios of PVDF: EC was conducted and compared with respect to thermal, mechanical and surface properties. |
|---|