Low cycle fatigue analysis of marine structures
Fatigue failure is a result of a repeated application of dynamic and fluctuating stresses which is of a lower intensity than those that would cause failure on a single application. Much research has been done on fatigue analysis for high cycle fatigue failure which accounts for failure that occurs f...
Saved in:
| 主要作者: | |
|---|---|
| 其他作者: | |
| 格式: | Final Year Project |
| 語言: | English |
| 出版: |
2012
|
| 主題: | |
| 在線閱讀: | http://hdl.handle.net/10356/49371 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 機構: | Nanyang Technological University |
| 語言: | English |
| 總結: | Fatigue failure is a result of a repeated application of dynamic and fluctuating stresses which is of a lower intensity than those that would cause failure on a single application. Much research has been done on fatigue analysis for high cycle fatigue failure which accounts for failure that occurs for loading cycles of more than 10^4, however, low cycle fatigue failure for marine structures had only been recognized in recent years due to the discovery of cracks in ships within a few years of delivery. |
|---|