The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings

Thin film coatings are commonly used in various applications and its performance is of high importance. The mechanical properties such as hardness often evaluated to determine the lifetime of a material. CrAlSiN is hard material and it is the successor of various thin film coatings such as CrN and C...

Full description

Saved in:
Bibliographic Details
Main Author: Chan, Kwan Yee.
Other Authors: Sam Zhang Shanyong
Format: Final Year Project
Language:English
Published: 2013
Subjects:
Online Access:http://hdl.handle.net/10356/54156
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Nanyang Technological University
Language: English
id sg-ntu-dr.10356-54156
record_format dspace
spelling sg-ntu-dr.10356-541562023-03-04T19:13:22Z The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings Chan, Kwan Yee. Sam Zhang Shanyong School of Mechanical and Aerospace Engineering DRNTU::Engineering Thin film coatings are commonly used in various applications and its performance is of high importance. The mechanical properties such as hardness often evaluated to determine the lifetime of a material. CrAlSiN is hard material and it is the successor of various thin film coatings such as CrN and CrAlN. CrAlSiN thin film is a hard but brittle material. Previous studies have shown the toughening effect of Ni on the CrAlSiN thin films. However, the performance of CrAlSiNiN at elevated temperature is still unknown. The objective of this experiment is to investigate the mechanical properties of Ni doped CrAlSiN thin film at elevated temperatures. In this experiment, the Ni content of Ni doped CrAlSiN thin film is increased from 0 to 39.8 at.%. At each concentration of Ni, Ni doped CrAlSiN thin film will be annealed at 500oC, 800oC, 900oC and 1000oC. The microstructure of Ni doped CrAlSiN thin film is studied using FESEM and it showed that when Ni concentration is increased, the surface morphology become grainier. When annealing temperature of Ni doped CrAlSiN thin film is increased, the surface of the thin film becomes very rough. The mean hardness of Ni doped CrAlSiN thin film decreases from 39.1±0.8 GPa to 14.9±2.6 GPa when amount of Ni doped increased from 0 to 39.8 at.%. However, hardness of Ni doped CrAlSiN thin film increases when it is annealed at 500oC and 800oC. However, hardness of Ni doped CrAlSiN thin film decreased when annealed at 900oC and 1000oC. The reduction in hardness when annealed at high temperatures could be due to destruction of surface at high temperatures. Bachelor of Engineering (Mechanical Engineering) 2013-06-14T04:20:20Z 2013-06-14T04:20:20Z 2013 2013 Final Year Project (FYP) http://hdl.handle.net/10356/54156 en Nanyang Technological University 59 p. application/pdf
institution Nanyang Technological University
building NTU Library
continent Asia
country Singapore
Singapore
content_provider NTU Library
collection DR-NTU
language English
topic DRNTU::Engineering
spellingShingle DRNTU::Engineering
Chan, Kwan Yee.
The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
description Thin film coatings are commonly used in various applications and its performance is of high importance. The mechanical properties such as hardness often evaluated to determine the lifetime of a material. CrAlSiN is hard material and it is the successor of various thin film coatings such as CrN and CrAlN. CrAlSiN thin film is a hard but brittle material. Previous studies have shown the toughening effect of Ni on the CrAlSiN thin films. However, the performance of CrAlSiNiN at elevated temperature is still unknown. The objective of this experiment is to investigate the mechanical properties of Ni doped CrAlSiN thin film at elevated temperatures. In this experiment, the Ni content of Ni doped CrAlSiN thin film is increased from 0 to 39.8 at.%. At each concentration of Ni, Ni doped CrAlSiN thin film will be annealed at 500oC, 800oC, 900oC and 1000oC. The microstructure of Ni doped CrAlSiN thin film is studied using FESEM and it showed that when Ni concentration is increased, the surface morphology become grainier. When annealing temperature of Ni doped CrAlSiN thin film is increased, the surface of the thin film becomes very rough. The mean hardness of Ni doped CrAlSiN thin film decreases from 39.1±0.8 GPa to 14.9±2.6 GPa when amount of Ni doped increased from 0 to 39.8 at.%. However, hardness of Ni doped CrAlSiN thin film increases when it is annealed at 500oC and 800oC. However, hardness of Ni doped CrAlSiN thin film decreased when annealed at 900oC and 1000oC. The reduction in hardness when annealed at high temperatures could be due to destruction of surface at high temperatures.
author2 Sam Zhang Shanyong
author_facet Sam Zhang Shanyong
Chan, Kwan Yee.
format Final Year Project
author Chan, Kwan Yee.
author_sort Chan, Kwan Yee.
title The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
title_short The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
title_full The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
title_fullStr The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
title_full_unstemmed The influence of Ni concentration on the mechanical properties of Ni doped CrAlSiN coatings
title_sort influence of ni concentration on the mechanical properties of ni doped cralsin coatings
publishDate 2013
url http://hdl.handle.net/10356/54156
_version_ 1759855132793634816