Photocatalytic and adsorption performance of faceted cuprous oxide (Cu2O)
Cu2O particles of various facets were successfully synthesized via wet chemical methods; these included the cubic shaped particles with {100} facets, octahedral shaped {111} facets, rhombic dodecahedral shaped {110} facets and the truncated polyhedral particles with exposed {100}, {111} and {110}...
Saved in:
Main Author: | |
---|---|
Other Authors: | |
Format: | Theses and Dissertations |
Language: | English |
Published: |
2016
|
Subjects: | |
Online Access: | http://hdl.handle.net/10356/68672 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Nanyang Technological University |
Language: | English |
Summary: | Cu2O particles of various facets were successfully synthesized via wet chemical methods;
these included the cubic shaped particles with {100} facets, octahedral shaped {111} facets,
rhombic dodecahedral shaped {110} facets and the truncated polyhedral particles with
exposed {100}, {111} and {110} facets. In addition, spherical Cu2O with no specific facets
was also synthesized. In this thesis, the adsorption capability and the photocatalytic
performance were determined to understand the physical and chemical properties of Cu2O.
The adsorption performance of the Cu2O particles in methyl orange (MO) solution is likely
due to the difference in the surface charges. The MO, which is an anion dye, were attached to
the positively charge surface of the Cu2O particles via electrostatic attraction. Among the
faceted Cu2O particles, the octahedral shaped Cu2O was found to adsorb more anions
probably due to the highest surface charges it possesses, which ranged from 19.7 to 33.0 mV.
The adsorption kinetic of the octahedral shaped Cu2O was also studied; the adsorption
equilibrium was calculated to be 96.42 mg/g following the Langmuir model, which indicates
monolayer adsorption. Several observations were concluded in the photocatalytic
performance of the faceted Cu2O particles. Firstly, the Cu2O of spherical shaped did not
possess any photocatalytic activity. This could be due to the agglomeration of nanoparticles
that potentially hinder the photocatalytic active sites. Secondly, series of experiments have
been carried out to prove that cubic shaped Cu2O was indeed visible light active. Thirdly,
compared to the rest of the Cu2O samples, Cu2O particle with the octahedral shape was
observed to perform better in dye degradation under visible light irradiation. This might be
because of the oxidation band potentials of the octahedral shaped Cu2O (+0.727 eV) particles
which lie below of the MO solution (+0.711 eV) and thus, the photogenerated electron-hole
pairs could be efficiently used to degrade the MO solution effectively. For the rest of the samples (cubic (+0.597 eV), rhombic dodecahedral (+0.547 eV) and truncated polyhedral
(+0.537eV)) whose oxidation band potentials lie above MO, only the photogenerated electron
was consumed during the dye degradation process. As such, it might slow down the entire
photocatalytic processs. Lastly, the stability of Cu2O particles under solar light irradation was
accessed. It was observed that the precipitates that formed on the surface of the Cu2O
particles were mainly Cu(OH)2 nanoparticles and CuO. The photocorrosion products
produced during dye degradation hinder the photocatalytic activity of Cu2O. The addition of
methanol solution, a well-known hole scavenger, has shown to have alleviated the corrosion
attack on Cu2O. This indicates that the photocatalytically generated holes were responsible
for the photocorrosion of Cu2O. In order to prolong the stability of Cu2O, it is therefore
necessary to have hole scavengers such as methanol to suppress the photocorrosion. |
---|