Improved densification and thermoelectric performance of In5SnSbO12 via Ga doping

In5SnSbO12 is being considered for use in thermoelectric applications. It has a satisfactory electrical conductivity and is expected to possess low thermal conductivity. However, it is difficult to densify In5SnSbO12 by conventional solid-state reaction method. In this work, we demonstrated that Ga...

Full description

Saved in:
Bibliographic Details
Main Authors: Zhu, Beibei, Zhang, Tianshu, Luo, Yubo, Wang, Yu, Tan, Thiam Teck, Donelson, Richard, Hng, Huey Hoon, Li, Sean
Other Authors: School of Materials Science & Engineering
Format: Article
Language:English
Published: 2019
Subjects:
Online Access:https://hdl.handle.net/10356/82849
http://hdl.handle.net/10220/48154
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Nanyang Technological University
Language: English
Description
Summary:In5SnSbO12 is being considered for use in thermoelectric applications. It has a satisfactory electrical conductivity and is expected to possess low thermal conductivity. However, it is difficult to densify In5SnSbO12 by conventional solid-state reaction method. In this work, we demonstrated that Ga doping could increase the relative density of In5SnSbO12, from ~ 60% (x = 0) to ~ 90% (x = 0.1). The improved densification may be attributable to the increased cationic occupancy after the addition of Ga and the reduced grain size induced by the presence of the secondary phase Ga2In6Sn2O16. The improved relative density led to a significant reduction in electrical resistivity; for example, for x = 0.1, the lowest electrical resistivity was ~ 0.002 Ω cm at 973 K, which was five times lower than that of the undoped sample (x = 0). The resultant power factor of this sample had a value of 3.4 × 10−4 Wm−1 K−2 at 973 K, which was nearly four times higher than that of the undoped sample. Although thermal conductivities were increased with Ga doping due to the enhanced densification, they were lower than that of In2O3. The highest thermoelectric performance was achieved in the sample with x = 0.05, specifically zT ~ 0.17 at 973 K. These results indicate that the addition of Ga to In5SnSbO12 results in a material which is more promising for thermoelectric applications.