Enhanced thermopower of graphene films with oxygen plasma treatment

• المؤلفون الرئيسيون: Ajayan, Pulickel M., Xiao, Ni, Dong, Xiaochen, Song, Li, Liu, Dayong, Tay, Yee Yan, Wu, Shixin, Li, Lain-Jong, Zhao, Yang, Yu, Ting, Zhang, Hua, Huang, Wei, Hng, Huey Hoon, Yan, Qingyu
• مؤلفون آخرون: School of Materials Science & Engineering
• التنسيق: مقال
• اللغة: English
• منشور في: 2012
• الموضوعات: DRNTU::Engineering::Materials::Nanostructured materials; DRNTU::Engineering::Materials::Plasma treatment
• الوصول للمادة أونلاين: https://hdl.handle.net/10356/93781; http://hdl.handle.net/10220/7452
• المؤسسة: Nanyang Technological University

In this work, we show that the maximum thermopower of few layers graphene (FLG) films could be greatly enhanced up to ∼700 μV/K after oxygen plasma treatment. The electrical conductivities of these plasma treated FLG films remain high, for example, ∼104 S/m, which results in power factors as high as ∼4.5 x 10-3 W K-2 m-1. In comparison, the pristine FLG films show a maximum thermopower of ∼80 μV/K with an electrical conductivity of ∼5 x 104 S/m. The proposed mechanism is due to generation of local disordered carbon that opens the band gap. Measured thermopowers of single-layer graphene (SLG) films and reduced graphene oxide (rGO) films were in the range of -40 to 50 and -10 to 20 μV/K, respectively. However, such oxygen plasma treatment is not suitable for SLG and rGO films. The SLG films were easily destroyed during the treatment while the electrical conductivity of rGO films is too low, which makes FLG films unique for possible TE applications.