Effects of Ti/Co and Co/Ti systems on the germanosilicidation of poly-Si capped poly-Si1−xGex substrate
Ti/Co and Co/Ti bilayered systems were used for the formation of Co germanosilicide on polysilicon buffered poly-Si1−xGex (x=0.2, 0.3) gate stacks. In both cases, substantial Ge was found to segregate to the grain boundaries at the surface of the polycrystalline silicide (i.e., CoSiGe) films, result...
Saved in:
| Main Authors: | , , |
|---|---|
| 其他作者: | |
| 格式: | Article |
| 語言: | English |
| 出版: |
2013
|
| 主題: | |
| 在線閱讀: | https://hdl.handle.net/10356/97519 http://hdl.handle.net/10220/10503 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 機構: | Nanyang Technological University |
| 語言: | English |
| 總結: | Ti/Co and Co/Ti bilayered systems were used for the formation of Co germanosilicide on polysilicon buffered poly-Si1−xGex (x=0.2, 0.3) gate stacks. In both cases, substantial Ge was found to segregate to the grain boundaries at the surface of the polycrystalline silicide (i.e., CoSiGe) films, resulting in a substantial degradation in the sheet resistance and a poor quality of the silicide films. It is shown that Ge is probably being expelled from the poly-SiGe grain and segregates to the grain boundaries during the annealing process, leading to the undesirable sheet resistance and poor film morphology observed from the Co germanosilicide films. |
|---|