Fabrication and properties of high quality transparent Ho:YAG ceramics
High quality holmium doped Yttrium Aluminum Garnet (YAG) transparent ceramics were fabricated by a reactive sintering method under vacuum. Fully dense Ho:YAG ceramics with the average grain size of ~ 10 μm were obtained after vacuum sintering at 1780 for 8 h. The optical properties, microstructures...
Saved in:
Main Authors: | , , , , , , |
---|---|
Other Authors: | |
Format: | Article |
Language: | English |
Published: |
2013
|
Online Access: | https://hdl.handle.net/10356/97617 http://hdl.handle.net/10220/13222 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Nanyang Technological University |
Language: | English |
Summary: | High quality holmium doped Yttrium Aluminum Garnet (YAG) transparent ceramics were fabricated by a reactive sintering method under vacuum. Fully dense Ho:YAG ceramics with the average grain size of ~ 10 μm were obtained after vacuum sintering at 1780 for 8 h. The optical properties, microstructures and photoluminescence spectra of the fabricated Ho:YAG ceramics were investigated. The transmittances of Ho:YAG ceramic are higher than 82% at 400 nm and 84% at 2400 nm. The absorption coefficient was 1.32 cm-1 for 1.5 at.% Ho:YAG at 1907 nm. And the absorption cross section of the Ho:YAG ceramic is 0.645×10-20 cm2. |
---|