Stress corrosion cracking behavior in 2297 Al-Cu-Li alloy at different grain orientations

• المؤلفون الرئيسيون: ZHANG JIAYI, Wang, Bin, Yi, Danqing
• مؤلفون آخرون: MECHANICAL ENGINEERING
• التنسيق: مقال
• اللغة: English
• منشور في: ELSEVIER SCIENCE SA 2019
• الموضوعات: Science & Technology; Technology; Nanoscience & Nanotechnology; Materials Science, Multidisciplinary; Metallurgy & Metallurgical Engineering; Science & Technology - Other Topics; Materials Science; 2297 Al-Cu-Li alloy; Stress corrosion cracking; Ductility; Annealing; Texture; HYDROGEN-INDUCED CRACKING; CRYSTALLOGRAPHIC TEXTURE; BOUNDARY-CHARACTER; ANODIC-DISSOLUTION; PIPELINE STEEL; SUSCEPTIBILITY; STRENGTH; RECRYSTALLIZATION; MICROSTRUCTURE; RESISTANCE
• الوصول للمادة أونلاين: https://scholarbank.nus.edu.sg/handle/10635/162226
• المؤسسة: National University of Singapore

10.1016/j.msea.2019.138252