Study of a Pd-Ag-Sb system alloy for metal-ceramics
The present study is aimed at developing a palladium silver based alloy containing antimony and other elements for metal-ceramics. Composition 54.2Pd-36.2Ag-4.7Sb-2.9In-1.0Sn-1.0Ga++ + (alloy No. 10) was finally selected as the best for practical applications. Liquidus and solidus temperatures of th...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.ncbi.nlm.nih.gov/pubmed/3502482 http://cmuir.cmu.ac.th/handle/6653943832/1115 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | The present study is aimed at developing a palladium silver based alloy containing antimony and other elements for metal-ceramics. Composition 54.2Pd-36.2Ag-4.7Sb-2.9In-1.0Sn-1.0Ga++ + (alloy No. 10) was finally selected as the best for practical applications. Liquidus and solidus temperatures of this alloy were 1,250 degrees C and 1,087 degrees C. Under fired conditions, the Vickers hardness number, tensile strength, and elongation were 270, 647 MPa, and 3.4%, respectively. In the temperature range from 20 degrees C to 600 degrees C, the thermal expansion rate was 0.87%, and the thermal expansion coefficient was 15.0 X 10(-6)/degrees C. The mechanical and manipulation properties of this alloy were satisfactory for clinical applications. |
|---|