Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses
© 2016 The Chinese Society of Rare Earths. Glasses were prepared from the compositions of 25Gd 2 O 3 -10CaO-10SiO 2 -(55-x)B 2 O 3 -xDy 2 O 3 (where x is 0.0 mol.%-1.0 mol.%) by the conventional melt-quenching technique at 1400 °C. The results demonstrated the increase in the glass density with res...
Saved in:
Main Authors: | , , , , |
---|---|
Format: | Journal |
Published: |
2017
|
Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84975087398&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/41848 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
id |
th-cmuir.6653943832-41848 |
---|---|
record_format |
dspace |
spelling |
th-cmuir.6653943832-418482017-09-28T04:23:47Z Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses Kaewkhao J. Wantana N. Kaewjaeng S. Kothan S. Kim H. © 2016 The Chinese Society of Rare Earths. Glasses were prepared from the compositions of 25Gd 2 O 3 -10CaO-10SiO 2 -(55-x)B 2 O 3 -xDy 2 O 3 (where x is 0.0 mol.%-1.0 mol.%) by the conventional melt-quenching technique at 1400 °C. The results demonstrated the increase in the glass density with respect to the increase in the doping concentrations of Dy 2 O 3 . Nine absorption bands were observed. The emission spectra of the developed glass showed two strong peaks at 577 nm ( 4 F 9/2 → 6 H 13/2 ) and 482 nm ( 4 F 9/2 → 6 H 15/2 ). The highest emission intensity was observed from the developed glass prepared at 0.4 mol.% of Dy 2 O 3 , as the efficient energy transfer took place from Gd 3+ to Dy 3+ . From the X-ray induced optical luminescence, the emission spectra were identical to those from PL measurements, but with the highest intensity observed from the glass quenched at 0.45 mol.% of Dy 2 O 3 . Finally, the integral scintillation efficiency of the developed glass was determined at 27% of that of the commercially available BGO crystal. 2017-09-28T04:23:47Z 2017-09-28T04:23:47Z 2016-06-01 Journal 10020721 2-s2.0-84975087398 10.1016/S1002-0721(16)60065-0 https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84975087398&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/41848 |
institution |
Chiang Mai University |
building |
Chiang Mai University Library |
country |
Thailand |
collection |
CMU Intellectual Repository |
description |
© 2016 The Chinese Society of Rare Earths. Glasses were prepared from the compositions of 25Gd 2 O 3 -10CaO-10SiO 2 -(55-x)B 2 O 3 -xDy 2 O 3 (where x is 0.0 mol.%-1.0 mol.%) by the conventional melt-quenching technique at 1400 °C. The results demonstrated the increase in the glass density with respect to the increase in the doping concentrations of Dy 2 O 3 . Nine absorption bands were observed. The emission spectra of the developed glass showed two strong peaks at 577 nm ( 4 F 9/2 → 6 H 13/2 ) and 482 nm ( 4 F 9/2 → 6 H 15/2 ). The highest emission intensity was observed from the developed glass prepared at 0.4 mol.% of Dy 2 O 3 , as the efficient energy transfer took place from Gd 3+ to Dy 3+ . From the X-ray induced optical luminescence, the emission spectra were identical to those from PL measurements, but with the highest intensity observed from the glass quenched at 0.45 mol.% of Dy 2 O 3 . Finally, the integral scintillation efficiency of the developed glass was determined at 27% of that of the commercially available BGO crystal. |
format |
Journal |
author |
Kaewkhao J. Wantana N. Kaewjaeng S. Kothan S. Kim H. |
spellingShingle |
Kaewkhao J. Wantana N. Kaewjaeng S. Kothan S. Kim H. Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
author_facet |
Kaewkhao J. Wantana N. Kaewjaeng S. Kothan S. Kim H. |
author_sort |
Kaewkhao J. |
title |
Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
title_short |
Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
title_full |
Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
title_fullStr |
Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
title_full_unstemmed |
Luminescence characteristics of Dy<sup>3+</sup> doped Gd<inf>2</inf>O<inf>3</inf>-CaO-SiO<inf>2</inf>-B<inf>2</inf>O<inf>3</inf> scintillating glasses |
title_sort |
luminescence characteristics of dy<sup>3+</sup> doped gd<inf>2</inf>o<inf>3</inf>-cao-sio<inf>2</inf>-b<inf>2</inf>o<inf>3</inf> scintillating glasses |
publishDate |
2017 |
url |
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84975087398&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/41848 |
_version_ |
1681422078235901952 |