Influence of sintering temperature on electrical properties of modified-PZT piezoelectric ceramics
© 2016 Trans Tech Publications, Switzerland. In this research, the effects of sintering temperature on phase structure, densification, microstructure, mechanical and electrical properties of modified-PZT ceramics were investigated. All ceramics were prepared by a conventional mixed oxide amend sinte...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Book Series |
| Published: |
2017
|
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84988566103&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/42609 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2016 Trans Tech Publications, Switzerland. In this research, the effects of sintering temperature on phase structure, densification, microstructure, mechanical and electrical properties of modified-PZT ceramics were investigated. All ceramics were prepared by a conventional mixed oxide amend sintered at various temperatures from 1150 - 1250°C. XRD pattern indicated that completely solid solution occurred for all samples and the ceramics exhibited a single perovskite without any secondary phases. At lower sintering temperature, the dominant phase was rhombohedral while tetragonal phase became dominant at higher temperature. Grain size tended to increase with increasing sintering temperature. The dielectric, ferroelectric and piezoelectric properties were also increased with increasing sintering temperature. In addition, the highest low field d 33 of 620 pC/N of was observed for the 1250°C sample. |
|---|