Thermogravimetry analysis, compressive strength and thermal conductivity tests of non-autoclaved aerated Portland cement-fly ash-silica fume concrete
© 2015 Akadémiai Kiadó, Budapest, Hungary. This paper reports the investigated thermogravimetry analysis, compressive strength and thermal conductivity tests of non-autoclaved aerated Portland cement-fly ash-silica fume concrete. The mixes were cured in water and air for 3, 7 and 28 days. Thermograv...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84941995882&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/44128 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2015 Akadémiai Kiadó, Budapest, Hungary. This paper reports the investigated thermogravimetry analysis, compressive strength and thermal conductivity tests of non-autoclaved aerated Portland cement-fly ash-silica fume concrete. The mixes were cured in water and air for 3, 7 and 28 days. Thermogravimetry results showed that calcium silicate hydrate (C-S-H), ettringite, gehlenite (C < inf > 2 < /inf > ASH < inf > 8 < /inf > ), calcium hydroxide [Ca(OH) < inf > 2 < /inf > ] and calcium carbonate (CaCO < inf > 3 < /inf > ) phases were detected in all mixes. The compressive strength and thermal conductivity of aerated Portland cement-fly ash-silica fume concrete increased when compared with aerated Portland cement-fly ash concrete after 28 days. The compressive strength and thermal conductivity of aerated concrete cured in water had higher values than air-cured specimens. X-ray diffraction and thermogravimetry showed that Ca(OH) < inf > 2 < /inf > decreased with increased silica fume content. This is due to the increased pozzolanic reaction when compared with the Portland cement-fly ash mixes, which corresponds to an increase in compressive strength and thermal conductivity. |
|---|