Influence of composition and isothermal sintering on the properties of hydroxyapatite bioceramic bodies

• Main Authors: Rungsarit Koonawoot, Cherdsak Saelee, Sakdiphon Thiansem, Sittiporn Punyanitya
• Format: Book Series
• Published: 2018
• Online Access: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84904165590&origin=inward; http://cmuir.cmu.ac.th/jspui/handle/6653943832/45353
• Institution: Chiang Mai University

This work reports the influence of chemical composition and sintering schedule on the properties of sintered bodies of hydroxyapatite (HA) bioceramic. The method of preparing sintered bodies by solid state reaction and uniaxial pressing. The raw material used calcium carbonate (CaCO 3 ) and ammonium dihydrogen phosphate (NH 4 H 2 PO 4 ) powder as precursors. These powders were mixed at CaCO 3 : NH 4 H 2 PO 4 mass ratio of 1:0. 697, 1:0. 692, 1:0. 689, 1:0. 685 and 1:0. 68, respectively. The compositions in the temperatures range of 800-1300 °C for 3 hour. The sintered bodies were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), and Fourier transform infrared spectroscopy (FTIR). Properties including phase, microstructures, porosity and bending strength of the samples. The results show that green bodies can be sintered at 1150 °C for 3 hours. This temperature found that crystals growth, highest of HA phase content in sintered bodies, good density and high efficiency strength properties. © (2014) Trans Tech Publications, Switzerland.