Thermoelectric and optical properties of CuAlO<inf>2</inf>synthesized by direct microwave heating
A single phase of delafossite CuAlO 2 (CAO) was successfully synthesized by a 600 W microwave radiation for 20 min. The CAO sample was composed of quite distorted single-crystalline plates with 200-350 nm thick. Its atomic vibrations were detected at 760 and 550 cm -1 belonging to Al-O and Cu-O stre...