การสังเคราะห์และการหาลักษณะเฉพาะของโครงสร้างนาโนซิงก์ออกไซด์โดยวิธีตกตะกอนโดยตรงเพื่อประยุกต์เป็นเซลล์แสงอาทิตย์ชนิดสีย้อมไวแสง

In this work, zinc oxide (ZnO) nanostructures were prepared by direct precipitation method. First, the ZnO precursors were synthesized by reaction of 0.4 M of zinc nitrate hexahydrate (Zn(NO3)2•6H2O) with various ammonium hydrogen carbonate (NH4HCO3) concentration in the range of 0.1251 M. Then, th...

全面介紹

Saved in:
書目詳細資料
主要作者: ศักดา เขื่อนรอบเขต
其他作者: สุภาพ ชูพันธ์
格式: Theses and Dissertations
語言:Thai
出版: เชียงใหม่ : บัณฑิตวิทยาลัย มหาวิทยาลัยเชียงใหม่ 2018
主題:
在線閱讀:http://cmuir.cmu.ac.th/jspui/handle/6653943832/45987
標簽: 添加標簽
沒有標簽, 成為第一個標記此記錄!
機構: Chiang Mai University
語言: Thai
實物特徵
總結:In this work, zinc oxide (ZnO) nanostructures were prepared by direct precipitation method. First, the ZnO precursors were synthesized by reaction of 0.4 M of zinc nitrate hexahydrate (Zn(NO3)2•6H2O) with various ammonium hydrogen carbonate (NH4HCO3) concentration in the range of 0.1251 M. Then, the precursors were calcined at 400C during 1 h to obtain ZnO nanostructures. After that, field emission scanning electron microscopy (FE-SEM), X-ray diffractometry (XRD), UV-vis spectroscopy and Raman spectroscopy were used to investigate morphology, crystallinity, optical properties and structures properties of ZnO nanostructures, respectively. The morphology of ZnO nanostructures exhibited particle– and rod–like morphology with their mean diameter increased from 53 nm to 5 µm by increasing NH4HCO3 concentration. In addition, ZnO nanostructures obtained by using 0.25 M of NH4HCO3 had minimum mean diameter of 53  14 nm suggesting the optimum condition. XRD patterns of the precursors showed the (200), (020), (021), (002) and (510) peaks that corresponds to the diffraction patterns of zinc carbonate hydroxide (Zn5(OH)6(CO3)2; JCPDS, No. 19-1458). After calcinations, XRD patterns showed the (100), (002), (101) and (102) peaks, attributes to the diffraction pattern of ZnO (JCPDS, No. 89-1397). In addition, transmittance value was decreased by increasing NH4HCO3 concentration. However, ZnO nanostructures obtained by using 0.25 M of NH4HCO3 had maximum transmittance of 36.8%, which related to minimum mean diameter. Finally, ZnO nanostructures were used to fabricate dye-sensitized solar cells (DSSCs). It was found that the maximum efficiency of 0.71% was observed for ZnO nanostructures obtained by using 0.25 M of NH4HCO3.