Effect of composition on phase formation, microstructure and dielectric properties of sol-bonded PZTN-PZT ceramics
The PZTN sol-powder was synthesized from a triol sol-gel process, while the ball milled PZT powder prepared from the reagent grade oxides of PbO, ZrO 2 and TiO 2 powders. The sol and balled milled powders were mixed at a ratio of 30:70, 50:50 and 70:30 by weight. The results showed that at a composi...