Fabrication of glass foams from industrial wastes used as insulating board
Insulating glass foam (IGF) was successfully fabricated by wet process. The starting proportion of 65 wt% waste glass, 12 wt% slag, 23 wt% commercial soap was added with 15 wt% Na 2 SiO 3 and represented then was sintered at 725 °C. The IGF had cellular structure with the macro-pore size at 0.428 m...
Saved in:
| Main Authors: | , , , |
|---|---|
| 格式: | Book Series |
| 出版: |
2018
|
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84884950255&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/47587 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Insulating glass foam (IGF) was successfully fabricated by wet process. The starting proportion of 65 wt% waste glass, 12 wt% slag, 23 wt% commercial soap was added with 15 wt% Na 2 SiO 3 and represented then was sintered at 725 °C. The IGF had cellular structure with the macro-pore size at 0.428 mm and thin cell walls. Density, thermal conductivity and compressive strength were 0.310 g/cm 3 , 0.130 W/m.K and 0.78 MPa, respectively. The average pore diameter and porosity increased with increasing the Na 2 SiO 3 concentration and the sintering temperature. On the other hand, the density, thermal conductivity and compressive strength were decreased. © (2013) Trans Tech Publications, Switzerland. |
|---|