Flame-made tungsten trioxide loaded zinc oxide nanoparticles in hybrid photovoltaic application

WO 3 -loaded ZnO nanoparticles containing 0, 0.25, 0.50, 0.75, 1.0 and 3.0 mol% of WO 3 were synthesized by Flame Spray Pyrolysis (FSP) from zinc naphthenate and tungsten ethoxide precursors under 5/5 (precursor/oxygen) flame condition. The crystalline phase, morphology and size of pure ZnO and WO...

Full description

Saved in:
Bibliographic Details
Main Authors: Chawarat Siriwong, Sukon Phanichphant
Format: Journal
Published: 2018
Online Access:https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84876566967&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/47991
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Chiang Mai University
Description
Summary:WO 3 -loaded ZnO nanoparticles containing 0, 0.25, 0.50, 0.75, 1.0 and 3.0 mol% of WO 3 were synthesized by Flame Spray Pyrolysis (FSP) from zinc naphthenate and tungsten ethoxide precursors under 5/5 (precursor/oxygen) flame condition. The crystalline phase, morphology and size of pure ZnO and WO 3 -loaded ZnO prepared by FSP were observed by XRD, BET, TEM and SEM. Moreover, these nanoparticles were successfully applied in hybrid photovoltaic devices as an electron acceptor. Theses devices were fabricated using conjugated polymers Poly(3-hexylthiophene) (P3HT) as an electron donor and poly (3,4-ethylenedioxythiophene): poly (styrenesulfonate) (PEDOT: PSS) as an electrode improver. Exciton dissociation of P3HT/ZnO hybrid photovoltaic that was deposited on an ITO substrate with PEDOT:PSS layer and capped with Al as a metal back electrode, was shown in figure below. The current-voltage characteristic of these devices showed that WO 3 could increase the number of photons actually converted to charge carriers that affect the power conversion efficiency. These results concluded that an appropriate amount of WO 3 loading could enhance the hybrid photovoltaic efficiency. Especially, the hybrid ZnO/P3HT photovoltaic device with 0.50 mol% WO 3 -loadeded ZnO as an electron acceptor exhibited maximum power conversion efficiency (η) of 0.411%.