Temperature and induced electric field dependence on the phase transition of 9/70/30, 9/65/35 and 9/60/40 PLZT ceramics
© 2018 Informa UK Limited, trading as Taylor & Francis Group. In this work, Pb 0.91 La 0.09 (Zr 1– x Ti x ) 0.9775 O 3 ceramics where x = 0.3, 0.35 and 0.4 (the composition near MPB) were prepared by solid solution method. After fabrication process, electrical property was measured by LCR mete...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85041115450&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/48388 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2018 Informa UK Limited, trading as Taylor & Francis Group. In this work, Pb 0.91 La 0.09 (Zr 1– x Ti x ) 0.9775 O 3 ceramics where x = 0.3, 0.35 and 0.4 (the composition near MPB) were prepared by solid solution method. After fabrication process, electrical property was measured by LCR meter. Polarization and induced strain behavior of the samples were investigated by using interferometry technique modified with Sawyer–Tower circuit at various temperatures. The results of dielectric, polarization and induced strain properties were due to the Zr/Ti ratios, which changed their behavior when temperature was varied (30–70 °C). The normal to macro-micro domains to relaxor and paraelectric phase transition was demonstrated which is related to linear or nonlinear increase of polarization and induced strain as a function of applied subswitching electric field. |
|---|