Development of engobe samples for Dan Kwian ceramic body
This paper developed engobe samples for Dan Kwian ceramic body. Kaolinite clay, zirconium silicate, sodium feldspar and quartz were used as raw materials which were varied to obtain various samples. Mix proportion was designed by the square sampling method to obtain 16 samples. All samples were mill...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
Trans Tech Publications Ltd
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84901921203&partnerID=40&md5=4fb65e018b92109db8541eba16813db6 http://cmuir.cmu.ac.th/handle/6653943832/4869 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | This paper developed engobe samples for Dan Kwian ceramic body. Kaolinite clay, zirconium silicate, sodium feldspar and quartz were used as raw materials which were varied to obtain various samples. Mix proportion was designed by the square sampling method to obtain 16 samples. All samples were milled and fired at 1200°C under oxidation and reduction atmospheres. The results showed that the suitable engobe composition of kaolinite clay 10 wt%, zirconium silicate 10 wt%, sodium feldspar 40 wt% and quartz 40 wt% to produce good surface appearance for Dan Kwian ceramics. Engobe surfaces and the body had no defect both in the oxidation and reduction atmospheres. The color and engobe surface were opaque white and glossy, respectively. © (2014) Trans Tech Publications, Switzerland. |
|---|